Study on Catalytic Mechanism of Reducing Hematite by Carbon at Low Temperature

Guo Peimin; Zhao Pei; Zhang Dianwei

Volume 27 Issue 4

Oct. 2023

Turn off MathJax

Article Contents

Abstract

References

Article Navigation > IRON STEEL VANADIUM TITANIUM > 2006 > 27(4): 1-5

Chen Yong, Yuan Hongwei, Yang Subo, Chen Lu:Ying. Research on Dynamic Soft Reduction Technologies for Bloom Continuous Casting of Heavy Rail[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(1): 35-41.

Citation:

Guo Peimin, Zhao Pei, Zhang Dianwei. Study on Catalytic Mechanism of Reducing Hematite by Carbon at Low Temperature[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(4): 1-5.

Chen Yong, Yuan Hongwei, Yang Subo, Chen Lu:Ying. Research on Dynamic Soft Reduction Technologies for Bloom Continuous Casting of Heavy Rail[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(1): 35-41.

Citation:

Guo Peimin, Zhao Pei, Zhang Dianwei. Study on Catalytic Mechanism of Reducing Hematite by Carbon at Low Temperature[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(4): 1-5.

PDF( 383 KB)

Study on Catalytic Mechanism of Reducing Hematite by Carbon at Low Temperature

The State Key Laboratory lor Advanced Iron and Steel Processes and Malerials, Central lron and Steel Research Institute, Beijing 100081, China

Received Date: 2004-04-24

Abstract

Abstract

The catalytic mechanism of reducing hematite was elucidated by experiments of Boudouard reaction and reducing hematite by CO gas and carbon.The rate of gasification reaction and reduction reaction was increased and showed similar tendency after addition of the catalyst.The catalytic effect of K₂CO₃ or Na₂CO₃ is substantially better than that of CaCO₃.The adding of catalyst seems to improve reactivity of carbon for hematite reduction,then accelerates the Boudouard reaction and promotes indirect reaction and direct reaction of hematite reduction,finally accelerates the reduction of hematite.
- hematite,
- carbon,
- catalytic mechanism,
- reduction

FullText(HTML)

References(0)

References

Relative Articles

[1]	Li Hongguang, Xu Mingli, He Wei, Wang Zhangyin. Effects of solidification structure on MnS in heavy rail steel bloom[J]. IRON STEEL VANADIUM TITANIUM, 2024, 45(5): 151-157. doi: 10.7513/j.issn.1004-7638.2024.05.020
[2]	Li Hongguang, Xu Mingli, Feng Yuanchao, Zeng Wu. Analysis on the formation of V-shape segregation in rail steel bloom[J]. IRON STEEL VANADIUM TITANIUM, 2023, 44(5): 180-187. doi: 10.7513/j.issn.1004-7638.2023.05.027
[3]	Li Hongguang. Effect of Interaction Between Superheat Degree and Combined EMS on Dendritic Structure and Homogeneity of Heavy Rail Steel Bloom[J]. IRON STEEL VANADIUM TITANIUM, 2020, 41(2): 114-119. doi: 10.7513/j.issn.1004-7638.2020.02.021
[4]	Chen Liang, Song Bo, Chen Tianming, Li Yangzhou, Li Zhiqiang, Li Jianquan. Key Technologies of Macro Segregation Control in 320 mm×410 mm Continuous Casting Bloom for Railway Steel[J]. IRON STEEL VANADIUM TITANIUM, 2018, 39(1): 118-123. doi: 10.7513/j.issn.1004-7638.2018.01.021
[5]	Sun Yanhui, Li Shiwei, Liu Fengjun, Zhao Haiyang. Influence of Mold Electromagnetic Stirring on Carbon Segregation on Continuously Cast Blooms of Bearing Steel[J]. IRON STEEL VANADIUM TITANIUM, 2013, 34(3): 72-76,87. doi: 10.7513/j.issn.1004-7638.2013.03.015
[6]	Chen Yong, Wu Guorong, Pan Hong, Li Jianquan. Key Technologies for Square/Round Billet Continuous Casting[J]. IRON STEEL VANADIUM TITANIUM, 2013, 34(2): 54-61. doi: 10.7513/j.issn.1004-7638.2013.02.011
[7]	Chen Tianming, Chen Yong, Deng Jun, Yang Senxiang, Chen Liang, Li Qingchun, Ceng Jianhua. Trial Production of High Chromium Tube Steel by Convert-bloom Continuous Casting Process[J]. IRON STEEL VANADIUM TITANIUM, 2011, 32(2): 39-42.
[8]	Chen Yong, Xiao Mingfu, Wu Guorong. Dynamic Soft Reduction Technology for 360mm×450mm Bloom Caster[J]. IRON STEEL VANADIUM TITANIUM, 2010, 31(1): 62-68.
[9]	Chen Yong, Wu Guorong, Sun Yanhui. Measurement of the Solidified Shell Thickness in the Secondary Cooling Zone of Continuous Casting of Bloom[J]. IRON STEEL VANADIUM TITANIUM, 2009, 30(1): 60-63.
[10]	Chen Yong, Chen Jianping, Wu Guorong, Yang Subo. Key Technology Development for 360 mm×450 mm Bloom Caster at PISCO[J]. IRON STEEL VANADIUM TITANIUM, 2009, 30(2): 61-67.
[11]	CHEN Yong, YANG Subo, ZHU Miaoyong. Research on Secondary Cooling Technology for Continuous Casting of 360 mm× 450 mm Bloom[J]. IRON STEEL VANADIUM TITANIUM, 2008, 29(4): 42-47.
[12]	Chen Yong, Yang Subo. Influence of Mold Electromagnetic Stirring Structure on Internal Quality of Continuously Cast Bloom[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(3): 42-46.
[13]	Chen Yong, Yang Subo. Research on Secondary Cooling Technologies for Bloom Continuous Casting of High Vanadium and Nitrogenous Weathering Steel[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(4): 36-41.
[14]	Chen Yong, Yang Subo, Li Jianquan, Chen Lu:Ying. Research on Mold Electromagnetic Stirring Technologies for Bloom Continuous Casting of Heavy Rail[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(4): 14-20,24.
[15]	Chen Yong, Yang Subo, Li Jianquan, Chen Lu:Ying. Research on Secondary Cooling Technologies for Continuous Bloom Casting[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(3): 31-37.
[16]	CHEN Yong, ZHANG Da-de, YANG Su-bo, LI Gui-jun, LI Jian-quan. OPTIMIZATION OF MOLD COOLING PROCESS AT BLOOM CONTINUOUS CASTING[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(4): 20-23.
[17]	CHEN Yong, LI Gui-jun, YANG Su-bo, WENG Jian-jun, CHEN Lu-ying. KEY TECHNOLOGIES FOR BLOOM CONTINUOUS CASTING AND ITS APPLICATION[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(1): 1-6.
[18]	CHEN Yong, LI Gui-jun, ZHAO Ke-wen. RESEARCH ON PRODUCTION OF 300 km/h HEAVY RAIL USING CONTINUOUSLY CAST ROUND BLOOM[J]. IRON STEEL VANADIUM TITANIUM, 2003, 24(4): 25-30.
[19]	CHEN Yong, LI Gui-jun, GOU Shu-yun. TECHNOLOGIES FOR IMPROVING QUALITY OF CONTINUOUSLY CAST HEAVY RAIL STEEL BLOOM[J]. IRON STEEL VANADIUM TITANIUM, 2002, 23(4): 41-46.
[20]	Dang Yuchun, Yang Jian, Zhao Rongjie. QUALITY OF STEEL FOR HEAVY RAIL NEEDS IMPROVING AT PANGANG[J]. IRON STEEL VANADIUM TITANIUM, 1997, 18(4): 9-13.