WANG Jian, NIE Mei-ying, YANG Sen-xiang, PENG Tao, LIU Xin, WANG Sheng, XIE Hai. STUDY OF RAISING TEMPERATURE OF MOLTEN STEEL IN CONVERTER WITH QUASI—GRAPHITE[J]. IRON STEEL VANADIUM TITANIUM, 2000, 21(3): 69-72.
Citation:
WANG Jian, NIE Mei-ying, YANG Sen-xiang, PENG Tao, LIU Xin, WANG Sheng, XIE Hai. STUDY OF RAISING TEMPERATURE OF MOLTEN STEEL IN CONVERTER WITH QUASI—GRAPHITE[J]. IRON STEEL VANADIUM TITANIUM, 2000, 21(3): 69-72.
WANG Jian, NIE Mei-ying, YANG Sen-xiang, PENG Tao, LIU Xin, WANG Sheng, XIE Hai. STUDY OF RAISING TEMPERATURE OF MOLTEN STEEL IN CONVERTER WITH QUASI—GRAPHITE[J]. IRON STEEL VANADIUM TITANIUM, 2000, 21(3): 69-72.
Citation:
WANG Jian, NIE Mei-ying, YANG Sen-xiang, PENG Tao, LIU Xin, WANG Sheng, XIE Hai. STUDY OF RAISING TEMPERATURE OF MOLTEN STEEL IN CONVERTER WITH QUASI—GRAPHITE[J]. IRON STEEL VANADIUM TITANIUM, 2000, 21(3): 69-72.
The raising temperature of molten steel in converter with quasi-graphite was investigated. The results obtained from 150 heats and expanded tests show the effect of raising temperature of molten steel with quasi-graphite is marked,the temperature compensation is 40.7℃ using 1 ton quasi-graphite.The use of quasi-graphite doesn’t influence slag formation and desulphurization and dephosphorization of molten steel during steelmaking process,can meet the requirements of steelmaking and slag splashing process.