DETERMINATION OF OXYGEN POTENTIAL FOR PANZHIHUA IRON ANK STEEL Co. BLAST FURNACE METAL ANK SLAG

Du Hegui; Zhang Ziping

Volume 16 Issue 3

Sep. 1995

Turn off MathJax

Article Contents

Abstract

References

Article Navigation > IRON STEEL VANADIUM TITANIUM > 1995 > 16(3): 1-5,29

Chen Yong, Yuan Hongwei, Yang Subo, Chen Lu:Ying. Research on Dynamic Soft Reduction Technologies for Bloom Continuous Casting of Heavy Rail[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(1): 35-41.

Citation:

Du Hegui, Zhang Ziping. DETERMINATION OF OXYGEN POTENTIAL FOR PANZHIHUA IRON ANK STEEL Co. BLAST FURNACE METAL ANK SLAG[J]. IRON STEEL VANADIUM TITANIUM, 1995, 16(3): 1-5,29.

Chen Yong, Yuan Hongwei, Yang Subo, Chen Lu:Ying. Research on Dynamic Soft Reduction Technologies for Bloom Continuous Casting of Heavy Rail[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(1): 35-41.

Citation:

Du Hegui, Zhang Ziping. DETERMINATION OF OXYGEN POTENTIAL FOR PANZHIHUA IRON ANK STEEL Co. BLAST FURNACE METAL ANK SLAG[J]. IRON STEEL VANADIUM TITANIUM, 1995, 16(3): 1-5,29.

PDF( 282 KB)

DETERMINATION OF OXYGEN POTENTIAL FOR PANZHIHUA IRON ANK STEEL Co. BLAST FURNACE METAL ANK SLAG

Northeastern University

Available Online: 2023-12-07

Abstract

Abstract

The oxygen probe made specially,sealed by refractory cement and adopting ZrO₂ base solid electrolyte tube, reference electrode with Cr.Cr₂O₃ powders,Mo electrode lead wire,has a good measuring stability.By experiments,the oxygen potential for high TiO₂ containing blast furnace slag is determined,successfully.It shows,by the measured results, that the oxygen partial pressure of Panzhihua Iron and steel Co. blast furnace slag is about 1.01325×10^-9pa and is round 100 times higher than general blast furnace slag.
- oxygen potential of metal and slag,
- oxygen probe,
- solid electrolyte,
- reference electrode

FullText(HTML)

References(0)

References

Relative Articles

[1]	Li Hongguang, Xu Mingli, He Wei, Wang Zhangyin. Effects of solidification structure on MnS in heavy rail steel bloom[J]. IRON STEEL VANADIUM TITANIUM, 2024, 45(5): 151-157. doi: 10.7513/j.issn.1004-7638.2024.05.020
[2]	Li Hongguang, Xu Mingli, Feng Yuanchao, Zeng Wu. Analysis on the formation of V-shape segregation in rail steel bloom[J]. IRON STEEL VANADIUM TITANIUM, 2023, 44(5): 180-187. doi: 10.7513/j.issn.1004-7638.2023.05.027
[3]	Li Hongguang. Effect of Interaction Between Superheat Degree and Combined EMS on Dendritic Structure and Homogeneity of Heavy Rail Steel Bloom[J]. IRON STEEL VANADIUM TITANIUM, 2020, 41(2): 114-119. doi: 10.7513/j.issn.1004-7638.2020.02.021
[4]	Chen Liang, Song Bo, Chen Tianming, Li Yangzhou, Li Zhiqiang, Li Jianquan. Key Technologies of Macro Segregation Control in 320 mm×410 mm Continuous Casting Bloom for Railway Steel[J]. IRON STEEL VANADIUM TITANIUM, 2018, 39(1): 118-123. doi: 10.7513/j.issn.1004-7638.2018.01.021
[5]	Sun Yanhui, Li Shiwei, Liu Fengjun, Zhao Haiyang. Influence of Mold Electromagnetic Stirring on Carbon Segregation on Continuously Cast Blooms of Bearing Steel[J]. IRON STEEL VANADIUM TITANIUM, 2013, 34(3): 72-76,87. doi: 10.7513/j.issn.1004-7638.2013.03.015
[6]	Chen Yong, Wu Guorong, Pan Hong, Li Jianquan. Key Technologies for Square/Round Billet Continuous Casting[J]. IRON STEEL VANADIUM TITANIUM, 2013, 34(2): 54-61. doi: 10.7513/j.issn.1004-7638.2013.02.011
[7]	Chen Tianming, Chen Yong, Deng Jun, Yang Senxiang, Chen Liang, Li Qingchun, Ceng Jianhua. Trial Production of High Chromium Tube Steel by Convert-bloom Continuous Casting Process[J]. IRON STEEL VANADIUM TITANIUM, 2011, 32(2): 39-42.
[8]	Chen Yong, Xiao Mingfu, Wu Guorong. Dynamic Soft Reduction Technology for 360mm×450mm Bloom Caster[J]. IRON STEEL VANADIUM TITANIUM, 2010, 31(1): 62-68.
[9]	Chen Yong, Wu Guorong, Sun Yanhui. Measurement of the Solidified Shell Thickness in the Secondary Cooling Zone of Continuous Casting of Bloom[J]. IRON STEEL VANADIUM TITANIUM, 2009, 30(1): 60-63.
[10]	Chen Yong, Chen Jianping, Wu Guorong, Yang Subo. Key Technology Development for 360 mm×450 mm Bloom Caster at PISCO[J]. IRON STEEL VANADIUM TITANIUM, 2009, 30(2): 61-67.
[11]	CHEN Yong, YANG Subo, ZHU Miaoyong. Research on Secondary Cooling Technology for Continuous Casting of 360 mm× 450 mm Bloom[J]. IRON STEEL VANADIUM TITANIUM, 2008, 29(4): 42-47.
[12]	Chen Yong, Yang Subo. Influence of Mold Electromagnetic Stirring Structure on Internal Quality of Continuously Cast Bloom[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(3): 42-46.
[13]	Chen Yong, Yang Subo. Research on Secondary Cooling Technologies for Bloom Continuous Casting of High Vanadium and Nitrogenous Weathering Steel[J]. IRON STEEL VANADIUM TITANIUM, 2007, 28(4): 36-41.
[14]	Chen Yong, Yang Subo, Li Jianquan, Chen Lu:Ying. Research on Mold Electromagnetic Stirring Technologies for Bloom Continuous Casting of Heavy Rail[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(4): 14-20,24.
[15]	Chen Yong, Yang Subo, Li Jianquan, Chen Lu:Ying. Research on Secondary Cooling Technologies for Continuous Bloom Casting[J]. IRON STEEL VANADIUM TITANIUM, 2006, 27(3): 31-37.
[16]	CHEN Yong, ZHANG Da-de, YANG Su-bo, LI Gui-jun, LI Jian-quan. OPTIMIZATION OF MOLD COOLING PROCESS AT BLOOM CONTINUOUS CASTING[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(4): 20-23.
[17]	CHEN Yong, LI Gui-jun, YANG Su-bo, WENG Jian-jun, CHEN Lu-ying. KEY TECHNOLOGIES FOR BLOOM CONTINUOUS CASTING AND ITS APPLICATION[J]. IRON STEEL VANADIUM TITANIUM, 2004, 25(1): 1-6.
[18]	CHEN Yong, LI Gui-jun, ZHAO Ke-wen. RESEARCH ON PRODUCTION OF 300 km/h HEAVY RAIL USING CONTINUOUSLY CAST ROUND BLOOM[J]. IRON STEEL VANADIUM TITANIUM, 2003, 24(4): 25-30.
[19]	CHEN Yong, LI Gui-jun, GOU Shu-yun. TECHNOLOGIES FOR IMPROVING QUALITY OF CONTINUOUSLY CAST HEAVY RAIL STEEL BLOOM[J]. IRON STEEL VANADIUM TITANIUM, 2002, 23(4): 41-46.
[20]	Dang Yuchun, Yang Jian, Zhao Rongjie. QUALITY OF STEEL FOR HEAVY RAIL NEEDS IMPROVING AT PANGANG[J]. IRON STEEL VANADIUM TITANIUM, 1997, 18(4): 9-13.