Feng Keqin, Zhang Binghuai. THE BEHAVIOR OF Ti REDUCTION IN SMELTING REDUCTION SLAG OF THE SYSTEM CaO-Sio2-Al2O3-MgO-TiO2[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(4): 32-37,49.
Citation:
Feng Keqin, Zhang Binghuai. THE BEHAVIOR OF Ti REDUCTION IN SMELTING REDUCTION SLAG OF THE SYSTEM CaO-Sio2-Al2O3-MgO-TiO2[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(4): 32-37,49.
Feng Keqin, Zhang Binghuai. THE BEHAVIOR OF Ti REDUCTION IN SMELTING REDUCTION SLAG OF THE SYSTEM CaO-Sio2-Al2O3-MgO-TiO2[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(4): 32-37,49.
Citation:
Feng Keqin, Zhang Binghuai. THE BEHAVIOR OF Ti REDUCTION IN SMELTING REDUCTION SLAG OF THE SYSTEM CaO-Sio2-Al2O3-MgO-TiO2[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(4): 32-37,49.
Experiments have been conducted to study the behavior of titanium reduction between the CaO-SiO2-Al2O3-MgO-TiO2 slag and carbon saturated iron melts in the smelting reduction process. The influences of TiO2-content in the slag,slag basicity(CaO/SiO2),reduction temperature and quantity of iron bath on the titanium reduction have also been investigated.
Feng Keqin, Zhang Binghuai. THE BEHAVIOR OF Ti REDUCTION IN SMELTING REDUCTION SLAG OF THE SYSTEM CaO-Sio2-Al2O3-MgO-TiO2[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(4): 32-37,49.