Diao Risheng, Wang Jing, Li Hongfang. DESULPHURIZATION AND REDUCTION PROCESS BETWEEN TiO2-CONTAINING SLAG AND MOLTEN PIG IRON[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(1): 10-15.
Citation:
Diao Risheng, Wang Jing, Li Hongfang. DESULPHURIZATION AND REDUCTION PROCESS BETWEEN TiO2-CONTAINING SLAG AND MOLTEN PIG IRON[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(1): 10-15.
Diao Risheng, Wang Jing, Li Hongfang. DESULPHURIZATION AND REDUCTION PROCESS BETWEEN TiO2-CONTAINING SLAG AND MOLTEN PIG IRON[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(1): 10-15.
Citation:
Diao Risheng, Wang Jing, Li Hongfang. DESULPHURIZATION AND REDUCTION PROCESS BETWEEN TiO2-CONTAINING SLAG AND MOLTEN PIG IRON[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(1): 10-15.
The desulphurization and reduction process of synthetic titaniferous slag with molten pig iron have been studied simulating the temperature variation from the dropping zone to hearth of the blast furnace. The variation of [V],[Ti],[Si] and [S] contents during reaction and the relation between the slag composition and the desulphurization capacity, TiO2 reduction have been examined. A slag composition is recommended in order to decrease TiO2 reduction and preserve the desulphurizing capacity when smelting titanomagnetite with TiO2 content about 25% in the slag.
Diao Risheng, Wang Jing, Li Hongfang. DESULPHURIZATION AND REDUCTION PROCESS BETWEEN TiO2-CONTAINING SLAG AND MOLTEN PIG IRON[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(1): 10-15.
Diao Risheng, Wang Jing, Li Hongfang. DESULPHURIZATION AND REDUCTION PROCESS BETWEEN TiO2-CONTAINING SLAG AND MOLTEN PIG IRON[J]. IRON STEEL VANADIUM TITANIUM, 1994, 15(1): 10-15.
DownLoad: