TiCl4水解制取高纯TiO2微粉的研究

留言板

尊敬的读者、作者、审稿人, 关于本刊的投稿、审稿、编辑和出版的任何问题, 您可以本页添加留言。我们将尽快给您答复。谢谢您的支持!

姓名
邮箱
手机号码
标题
留言内容
验证码

TiCl₄水解制取高纯TiO₂微粉的研究

胡鸿飞, 锡淦, 许述林, 黄守华, 李大成, 全学军

文章导航 > 钢铁钒钛 > 1998 > 19(2): 13-19

郑德顺. 攀钢线材生产中金属工艺损耗状况及分析[J]. 钢铁钒钛, 1997, 18(1): 33-36,50.

引用本文:

胡鸿飞, 锡淦, 许述林, 黄守华, 李大成, 全学军. TiCl₄水解制取高纯TiO₂微粉的研究[J]. 钢铁钒钛, 1998, 19(2): 13-19.

Zheng Deshun. STATUS AND ANALYSIS OF METAL LOSS IN WIRE ROD PRODUCTION AT PANGANG[J]. IRON STEEL VANADIUM TITANIUM, 1997, 18(1): 33-36,50.

Citation:

HU Hongfei, XI Gan, XU Shulin, HUANG Shouhua, LI Dacheng, QUAN Xuejun. DEVELOPMENT OF HIGH PURITY ULTRAFINE TiO₂ POWDER BY TiCl₄ HYDROLYSIS[J]. IRON STEEL VANADIUM TITANIUM, 1998, 19(2): 13-19.

郑德顺. 攀钢线材生产中金属工艺损耗状况及分析[J]. 钢铁钒钛, 1997, 18(1): 33-36,50.

引用本文:

胡鸿飞, 锡淦, 许述林, 黄守华, 李大成, 全学军. TiCl₄水解制取高纯TiO₂微粉的研究[J]. 钢铁钒钛, 1998, 19(2): 13-19.

Zheng Deshun. STATUS AND ANALYSIS OF METAL LOSS IN WIRE ROD PRODUCTION AT PANGANG[J]. IRON STEEL VANADIUM TITANIUM, 1997, 18(1): 33-36,50.

Citation:

HU Hongfei, XI Gan, XU Shulin, HUANG Shouhua, LI Dacheng, QUAN Xuejun. DEVELOPMENT OF HIGH PURITY ULTRAFINE TiO₂ POWDER BY TiCl₄ HYDROLYSIS[J]. IRON STEEL VANADIUM TITANIUM, 1998, 19(2): 13-19.

TiCl₄水解制取高纯TiO₂微粉的研究

1. 攀枝花钢铁研究院;
2. 四川联合大学

计量
- 文章访问数: 86
- HTML全文浏览量: 23
- PDF下载量: 3
- 被引次数: 0
出版历程
- 收稿日期: 1998-01-16
- 刊出日期: 1998-06-30

DEVELOPMENT OF HIGH PURITY ULTRAFINE TiO₂ POWDER BY TiCl₄ HYDROLYSIS

1. Panzhihua Iron and Steel Research Institute;
Sichuan Union University

摘要: 探讨了在有机分散剂存在下，采用氨水中和水解TiCl₄制备高纯TiO₂的工艺方法。研究了分散剂种类和用量，反应物浓度，加料方式,熟化温度和时间对TiO₂性能的影响。制取了纯度≥99.5％，粒径<1.0μ，近似球形的TiO₂微粉。100kg级的试验结果表明，TiO₂微粉的理化指标和制成的PTC电子元件的电性能均接近日本TDK公司同类产品的技术指标。
- 四氯化钛 /
- 水解 /
- 分散剂 /
- 高纯微细二氧化钛
Abstract: The process for preparation of high purity ultrafine TiO₂ powder by means of neutralization of hydrolyzed TiCl₄ solution with ammonia in the presence of organic dispersant was developed. The effects of the dispersant type and its consumption, concentration of reactants, feeding mode,maturing temperature and time on the properties of TiO₂ were investigated.The spheroidal TiO₂ powder was prepared whose purity is over 99.5%,particle diameter is less than 1.0μ,The results of 100kg grade test show the physicochemical properties of the ultrafine TiO₂ powder and the characteristics of PTC electronic component made from the TiO₂ powder approach the technical index of similar products of TDK Co. in Japan.
- titanic chloride /
- hydrolysis /
- dispersant /
- high purity ultrafine titanium oxide

参考文献(0)

资源附件(0)

WeChat

点击查看大图

计量

文章访问数: 86
HTML全文浏览量: 23
PDF下载量: 3
被引次数: 0

/

下载: 全尺寸图片幻灯片

分享

用微信扫码二维码

分享至好友和朋友圈

返回

本系统由北京仁和汇智信息技术有限公司开发

x 关闭永久关闭

《钢铁钒钛》版面费调整通知